Alec using CLR sounds like a great idea. I have been using vinegar to clean corroded pads,
but heavy corrosion I need to scrap them to expose fresh tin/copper.

I have a Laseractive pac I am working on with well over a hundred corroded pads.
If I dab each contact with some CLR how long should I let it sit?